Changsha Honchon Technology Co., Ltd

Ultra Translucent Zirconia has the highest translucency in all the white zirconia, which is highly aesthetic and appealing. Its glassy translucency makes it very suitable for making veneer, coping & anterior crown. Perfect match with Honchon UT 16 shade liquid. After processing and polishing, the teeth made by Ultra Translucent Zirconia could show soft reflective light under sunlight and look more pure.

 

Ultra Translucent Zirconia is one of the earliest products of our factory, Ultra Translucent Zirconia has gone through many technology revolutions in the past 15 years. With mature production skills and scientific formula, Ultra Translucent Zirconia is still hot sale while preshaded and multilayer zirconia has come out. It's highly praised by its trustworthy high strength, fine powder and wide application.

Color:	White
Aesthetic:	Ultra Translucent
Sintered Density：	6.0g/cm³
Bending Strength：	650Mpa
Light Transmittance：	49%
Sintering Temperature：	1530℃
Recommend Indications:	Inlay & Onlay & Partial Crown & Coping & Anterior Crown & Coping Bridge & Veneer & Full Contour Bridge ≤4 unit

 

Benefits of Ultra Translucent Zirconia：

High transparency: Ultra Translucent Zirconia has a light transmittance of up to 49%, making the dental restorations closer to natural teeth in appearance and providing excellent aesthetic results.

 

High strength: With a flexural strength of 650Mpa, Ultra Translucent Zirconia is stronger than many other dental materials and can withstand the pressure and wear of daily oral life, thereby extending the life of the restoration.

 

Versatility: This material is suitable for a variety of dental applications, including inlays, sleeves, partial crowns, anterior crowns, bridges, veneers, and up to four-unit full crown bridges, allowing dental professionals to choose the right restoration for different clinical needs.

 

High-quality ingredients: The main ingredients of Ultra Translucent Zirconia include zirconium oxide (ZrO2), hafnium oxide (HfO2) and yttrium oxide (Y2O3), of which the content of yttrium oxide is between 9% and 10%, ensuring the transparency and strength of the material.

 

High sintering temperature: The recommended sintering temperature is 1530°C, which helps the material achieve optimal physical properties, ensuring that the restoration is both strong and aesthetically pleasing.

 

Easy processing: Compatibility with other dental milling machines allows Ultra Translucent Zirconia to be easily shaped and processed to meet specific restoration needs.

 

Long-lasting beauty: Due to its excellent transparency and color properties, restorations made with Ultra Translucent Zirconia will maintain a natural and attractive appearance over time.

 

 

	Components	HT Plus
	ZrO2+HfO2+Y2O3	≥99%
	Y2O3	9%-10%
	Al2O3	＜0.05%
	Other Oxides	＜0.05%

 

 

 

Ultra Translucent Zirconia Sintering Curve
Sintering step	Start Temperature(℃)	End Temperature(℃)	Time(Min)	Rate(℃/Min)
Step 1	20	900	176	5
Step 2	900	1450	69	8
Step 3	1450	1450	120	0
Step 4	1450	1000	56	-8
Step 5	1000	20	151	-6.5

 

Please follow the sintering curve and notice the peek temperature is 1450℃. Any questions from you will be seriously treated and sincerely welcomed.

 

 

Advantage :

-- Premium quality zirconia powder
-- Cold isostatic pressed to ensure homogenous density and shrinkage distribution.
-- Easy to cut, no porcelain breakage, less scraps
-- More accurate scaling factor

 

Common Questions and Answers about Ultra Translucent Zirconia:

 

Q: What is ultra translucent zirconia?
A: Ultra translucent zirconia, also known as highly translucent or super translucent zirconia, is a type of zirconium dioxide ceramic that has been optimized for enhanced translucency. It is used in dental restorations to mimic the natural translucency of tooth enamel and provide a more aesthetically pleasing appearance.

 

Q: How does ultra translucent zirconia differ from traditional zirconia?
A: Traditional zirconia is known for its strength and durability but has a more opaque appearance. Ultra translucent zirconia has been engineered to allow more light to pass through, giving it an appearance closer to natural teeth. This is achieved by altering the grain size, adding specific types of yttria stabilization, and optimizing the sintering process.

 

 

http://www.zirconia-blank.com/